Just hooked my new miller 210 and was wondering what I should have the gas setting at. I am running argon mix. I have never welded with gas, but have done quite a bit with flux core wire. Any help would be appreciated.
Just hooked my new miller 210 and was wondering what I should have the gas setting at. I am running argon mix. I have never welded with gas, but have done quite a bit with flux core wire. Any help would be appreciated.
dont know what regulator you have but 20-25CFM is a good place to start. run it as low as possible without getting the "bubbily porus weld crap" otherwise its just waste
If you are welding in the garage and the air is still, 15 is just about right for the 210, I would not go up past 20. excess gas flow can actually adversley affect the puddle.
If you are welding in the garage and the air is still, 15 is just about right for the 210, I would not go up past 20. excess gas flow can actually adversley affect the puddle.
Yes, you just want to mask the area with the mix. You don't want the gas to rush across the surface. Each time you weld you will need different flows. Just use your judgement on how well the gas is masking your weld.
well the easiest way is just open the machine hood and look at the chart.that has always worked for me. the only time i ever adjust the psi is if i have to weld in the wind( not recomended), turn it up to make it over power the wind.
between 15 and 20 i run about 15 or 16 always works fine, and weld on a table not the garage floor, there is always a low draft along the floors that will disrupt the weld and cause bubbles